Aluminium Cut Wire Shots
We offer to our clients aluminum cut wire shot that is the ideal material for cleaning and reinforcing the surface of nonferrous metal casting parts. Made from superior grade aluminum wires, these are highly durable and long lasting. Offered at competent rates, we have the capability to offer them with customized specifications.
CUT WIRE SHOT SPECIFICATIONS
|
SIZE
|
|
|
|
Cut Wire
|
Cut Wire
|
Cut Wire
|
|
|
|
Designation
|
Designation
|
Designation
|
MATERIAL
|
|
( inch )
|
( mm )
|
Size
|
|
CW 12
|
0.30
|
S-110
|
Mild Steel
|
Type 1020
|
|
CW 14
|
0.35
|
S-130
|
Carbon Steel
|
Type 1070
|
|
CW 17
|
0.45
|
S-170
|
Stainless Steel
|
Type 302, Type 304,
|
|
CW 20
|
0.50
|
S-190
|
|
Type 430
|
|
CW 23
|
0.60
|
S-230
|
|
|
|
CW 28
|
0.70
|
S-280
|
|
|
|
CW 32
|
0.80
|
S-330
|
HARDNESS RANGE
|
|
CW 35
|
0.90
|
S-360
|
Mild Steel
|
24-30 HRC
|
|
CW 41
|
1.00
|
S-390
|
Carbon Steel
|
40-50/45-55 HRC
|
|
CW 47
|
1.20
|
S-460
|
Stainless Steel 302/304
|
32 HRC minimum
|
|
CW 54
|
1.40
|
S-550
|
|
|
|
CW 62
|
1.60
|
S-660
|
|
|
|
|
|
|
|
|
|
SHAPES
|
DESCRIPTION
|
|
SPECIFICATION- IS 5873/1970
|
|
|
As Cut (U)
|
Cylindrical with Shape Edge
|
|
SAE J 441 C W S
|
|
|
Normal ( C )
|
Corner pre round
|
|
SAE J 441 C W S
|
|
|
Conditioned (3C)
|
Almost Spherical
|
|
AMS 2431 / 3/ 4 & 8
|
|
COMPARISON BETWEEN CAST STEEL SHOTS & STEEL CUT WIRE SHOTS
|
CHARACTERSTIC
|
CAST STEEL SHOTS
|
STEEL CUT WIRE SHOTS
|
|
Raw Material
|
Basic Raw Material has far lower physical property & Composition,
obviously causes blowholes & porosity which makes the shots to fracture into small particle.
|
Raw Material is of exact composition, with-out any material defect (blow holes, porosity, shrinkage, etc.), & wears out nominally during it's use
|
|
Dust Generation
|
Higher Dust Generation
|
No Dust Generation
|
|
Environment Friendly
|
Deteriorates environment of work place and it's dust is considered hazardous to health
|
Environment Friendly
|
|
Performance Consistency
|
Consistent Performance not possible due to fast size deterioration
|
Consistent Performance
|
|
Time Consumption
|
Higher Consumption in shot Blasting/peening increases working cycle time
|
Reduced Time for Shot Blasting/Peening
|
|
Shot Consumption
|
Higher Consumption
|
Consumption decreases i.e.33% to 67% less to cast shots (case to case basis)
|
|
Inventory Cost
|
Higher Consumption requires high Inventory,more money & space as well
|
Lower Inventory required for the same job.
|
|
Operation Cost
|
Higher Operation cost
|
Lower Operation cost
|
|
Shape Variations
|
Shot being produced are of mixed size hence product is a mix of various spherical sizes.
|
All shot being made out of same wire are identical,no variation of size anywhere.
|
|
Hardness Variation
|
They have larger variation in hardness
|
Uniform hardness throughout.
|
|
Micro-Structure
|
In Micro-structure carbide always there.
|
Micro-structure is only Tempered martensite.
|
|
Grain Size
|
Grain size of cast shot is unstabilized
|
Due o drawing passes grain size is stabilised.
|
|